A strange pesh kabz

shayde78 · 13th January 2018, 08:40 PM

Interesting that this item has a very similar profile to mine posted here

My thoughts on the pitting are that it could have been caused by rust that formed where the wood of the sheath may have trapped moisture against the blade. Although much of the hilt is covered by the sheath, it tightens against the blade right where yours shows pitting. If someone has since polished away the rust, it may well look like your example.

Battara · 13th January 2018, 09:04 PM

I agree that there is a lot of pitting, and that it does look like someone has "painted" (?) over the active rust.

When I restore pieces with this type of pitting, I try to get down as much as possible, but know that there will always be a certain amount of pitting left. The reason is that if you remove all of the pitting, there might not be much of a blade left or the blade will be too thin to be useful depending on how deep the pitting goes.

shastardhari · 24th January 2018, 10:48 AM

Quote:

Originally Posted by Battara

I agree that there is a lot of pitting, and that it does look like someone has "painted" (?) over the active rust.

When I restore pieces with this type of pitting, I try to get down as much as possible, but know that there will always be a certain amount of pitting left. The reason is that if you remove all of the pitting, there might not be much of a blade left or the blade will be too thin to be useful depending on how deep the pitting goes.

Agreed!

13th January 2018, 08:40 PM	#1
shayde78 Member Join Date: Mar 2017 Posts: 445	Interesting that this item has a very similar profile to mine posted here My thoughts on the pitting are that it could have been caused by rust that formed where the wood of the sheath may have trapped moisture against the blade. Although much of the hilt is covered by the sheath, it tightens against the blade right where yours shows pitting. If someone has since polished away the rust, it may well look like your example.

13th January 2018, 09:04 PM	#2
Battara EAAF Staff Join Date: Dec 2004 Location: Louisville, KY Posts: 7,270	I agree that there is a lot of pitting, and that it does look like someone has "painted" (?) over the active rust. When I restore pieces with this type of pitting, I try to get down as much as possible, but know that there will always be a certain amount of pitting left. The reason is that if you remove all of the pitting, there might not be much of a blade left or the blade will be too thin to be useful depending on how deep the pitting goes.