Thoughts on this Keris

[A. G. Maisey]

Thanks Anthony, yes, at his best --- which was most definitely not always --- I consider this man to have been the best exponent of his generation of the classic Surakarta keris.

Here it is in full dress.

[David]

Thanks for showing that beautiful keris.
You haven't yet, and that is probably by intent, but are you willing to make any comments about the push dagger this young smith claims has retained the Widmanstätten pattern from the meteorite he used. It has always been my understanding that is not possible once forged, but my experience with actual forging is limited to a few simple projects done with old railroad spikes so i have no expertise to go on here. But it sure seems like a spurious claim to me.

[Seerp Visser]

To my knowlegde, the Widmanstatten structure disappeares at a temperature of about or some over 700 degrees C.
The materials for forging the dagger are too cold to forgeweld at that temperature.
Widmanstatten structures are formed by extremely slow cooling of the material during millions of years.
So the meteoritic material has been inserted in te dagger cold, or at least on a temperature lower than 700 degrees C.

[A. G. Maisey]

Spot on Seerp. Jerzy said pretty much the same thing about ID of meteorite after the forge weld process.

It is a really pretty keris David, in fact much better than the photo shows, that photo was done more than ten years ago, my equipment and understanding has improved a bit during the last 10 or 12 years.

As for our young wouldbe blade smith, I'd just as soon not comment, let other people teach him what's right & what's wrong.

[Anthony G.]

Originally Posted by A. G. Maisey

Thanks Anthony, yes, at his best --- which was most definitely not always --- I consider this man to have been the best exponent of his generation of the classic Surakarta keris.

Here it is in full dress.

I am lost for word. Even the dress is awesome.

[Gustav]

In A. Weihrauch's thesis there is a dokumentation of an experiment - they made a weld sample with different ferric materials, and one of them was an iron meteorite.

Even after forging and welding the Widmanstätten pattern is still recognisable in enlargement 500:1.

There is a remark "after a longer glow they (the W-patterns) disappear completely.".

[A. G. Maisey]

That is very interesting information Gustav.

I assume that Weihrauch was talking about welding in the forge?

It is interesting, but also confusing.

The weld temperature of iron is + 2500F (1400C) at and above this temperature the surface of the iron is beginning to show white, it is sticky and on the point of liquification

The weld temperature of most steels is + 1700F (900C) and it is into high orange in colour, the surface is sticky but not liquifying.

Nickel has a lower weld temperature than the steels, I'm not sure what the actual temperature is, but I'd guess +/- 200F lower, say around 1400F - 1600F.

So when we weld a piece of material like meteoritic material, that has nickel running through it we are welding the iron at more than 2500F and the nickel is also going to be at +2500F, however, the melting temperature of nickel is between 1600F & 1700F, so when the weld is taken, that nickel is already well past its melting point.

To take the weld, hammer blows on the surfaces of the material are required, initially only light, but increasing in force.

The colour of the iron when first hit will be close to white and it will be beginning to liquify.

Weihrauch has stated:- "after a longer glow they (the W-patterns) disappear completely."

To my mind it is truly miraculous that any Widmanstatten pattern remained in the material, even before it was hit with a hammer. If, of course, Weihrauch was talking about forge welding, not gas welds, nor electric welds.

To use meteoritic material in a blade it needs to be cleaned, this is achieved by folding and welding the billet of meteoritic material. In my experience it usually takes at least 7 welds before the meteoritic material is clean enough to use. So 7 or more welds, combined with quite heavy forging. Then more welding to attach the meteoritic material to the steel core.

I think I'll continue to back Prof. Piaskowski's opinion.

[Athanase]

I think that the only way to know the presence or not of meteoritic materials in a blade is by a very thorough analysis of the chemical composition (mass spectrometry). The meteorite still contains elements that are very rare on earth (like Iridium for example). The detection of its trace elements much greater proportion than for terrestrial materials could provide evidence.

[Ian]

Originally Posted by Athanase

I think that the only way to know the presence or not of meteoritic materials in a blade is by a very thorough analysis of the chemical composition (mass spectrometry). The meteorite still contains elements that are very rare on earth (like Iridium for example). The detection of its trace elements much greater proportion than for terrestrial materials could provide evidence.

Actually, X-ray fluorescence (XRF) would probably be the best analytical method as it is non-destructive, and would indicate the nature and amount of various metals detected at the surface of the blade. Small portable and hand-held devices are now available.

[A. G. Maisey]

Even though I have worked iron-nickel meteoric material in the forge I know almost nothing about meteors, as I commented earlier, I have never studied this material, I have only used it.

So this is a question, it is not a statement of opinion nor is it an attempt at debate, I simply want somebody who does truly understand the study of iron-nickel meteorites to give me an answer that can be supported with evidence.

I assisted Prof. Jerzy Piaskowski of Poland in his examination of S.E. Asian blade materials, over a period of more than 15 years. Jerzy was a noted historical metallurgist who worked at the Institute of Metallurgy in Krakow. Jerzy passed away in 2013, and he was about 90 when he left this world. His methods of examination were dated, and he did not have the benefit during his working life of the technology that is now available to us for the examination of minerals.

Jerzy's opinion was that it was not possible to identify with any certainty any iron-nickel material that had a meteoric origin after it had been through the process of multiple forge welds and heavy forging. All the minerals that can be found in an iron-nickel meteorite can be found on Earth.

Last year I heard from a friend who is a noted collector of minerals, that scientists in the USA had found a new mineral in an Australian meteorite (Wedderburn meteorite) that had not previously been found in nature on Earth, this mineral is called something like edscoti, it can be found in iron that has been through high temperature processing on Earth, but not in nature.

So even if we now do have a mineral that is unique to some meteorites and is not found in nature on Earth, will that assist in identifying meteoric material after that material has been through multiple forge welds and heavy forging? Personally, I rather think not.

Based upon what little I know about meteoric material, I feel that it would be a total impossibility to determine with certainty that material which has been repeatedly forge welded for up to perhaps ten times, and that has also been heavily forged could with certainty be identified as being of meteoric origin.

It might perhaps be possible to determine with a degree of possibility that a piece of material as described above could be of meteoric origin, but can such a determination be made with certainty?

As stated above, I am not opening a debate here, all I would like to see is an answer that can be supported with evidence from somebody who does truly understand the study of iron-nickel meteorites.

There has been ongoing discussion of this matter over many years in the keris community, and in other areas of study, such as archaeology , and some of the conclusions and opinions put forward have been utterly ridiculous.

It would be very nice to be able to put this matter to one side and either forget about it, or to be able to know that we can state with certainty that a piece of material that has been through extensive high temperature processing here on Earth can indeed be positively identified as being meteoric in origin.

[Seerp Visser]

The past years i made a study to the use of iron meteorite by making damast steel in general and the forging of iron meteorite in the blade of a kris in particular.
I made many tests on the way i estimate the Empus used in the past and some still do today.
The results of my study are published in a booklet (approx 50 pages, Dutch language) under the name "Het ijzer van de Goden".
It will be published within a month or two in English with the name "Iron of the Gods".

What the Widtmanstatten concerns, to my opinion the Widmanstatten will disappear as soon the iron transfers into a new crystal structure, the austenitic structure, at about 730 degrees C or approx 1350 F.
But i will check that the coming weeks by making some tests.

[A. G. Maisey]

Actually, I have never seen the W pattern in any of the meteoritic material that I worked on. Everything that I used to make blades was in small pieces that were put into the fire together and amalgamated into a single piece that was then amalgamated with other single pieces and worked into a clean billet.

So I did not study it, I only used it.

But what you found Seerp, certainly makes sense to me.

In Jawa, the way in which meteoritic material is worked is by taking small pieces and enclosing in an iron envelope which is then welded together and worked clean. The resultant billet is a combination of manufactured iron and meteor, ready to use as a pamor base. My method differed from the Javanese method in that I produced a billet of pure meteoritic material and then worked that with other ferric material to make the blade, or to combine with iron to produce pamor.

[A. G. Maisey]

Here is something worth a read:-

https://www.bladesmithsforum.com/ind...eteorite-iron/