[Edster]

Marc,

This is off topic, but since you are a blacksmith you no doubt have experience in applying stamps to metal. Your experience could help in identifying dates & origins of imported and locally made blades. The question: would a maker's mark or other stamp be applied with the strike of a hammer to a relative soft sword blade just after forging or after the blade had been quenched and drawn? We see marks attributed to a retailer after a European blade was imported, or maybe as fake marks to impute quality, etc. Also, some marks are a identified as rack or inventory stamps applied in an amory, etc.

Would a sword blade be softer at forte area that may not have been quenched and accept a stamp better? This may be why makers marks are often seen under langets.

Best regards,
Ed