Default My First Experience With Scarf Welding on a Moro Kriss

Scarf welding is not particularly uncommon on Malay sundang, but this is my first experience with it on a Moro kriss. The forte seems to be from steel more comparable to 'pamor' steel, but you can easily see where that stops and the more imaginative pattern weld begins.

The copper-wrapped hilt is unique as well.
Attached Images
      

Last edited by CharlesS; 17th April 2022 at 05:33 PM. Reason: pictures omitted
CharlesS is offline   Reply With Quote
Old 17th April 2022, 06:15 PM   #2
David R
Member
 
David R's Avatar
 
Join Date: Jan 2011
Posts: 1,079
Default

It's always interesting to see these sort of details. I wonder if this was a matter of using up material that was on hand, or a repair-recycle of a broken blade.
David R is offline   Reply With Quote
Old 17th April 2022, 07:47 PM   #3
kronckew
Member
 
kronckew's Avatar
 
Join Date: Mar 2006
Location: Room 101, Glos. UK
Posts: 4,184
Default

I'd like to see the other side of the blade near the tang/grip. The delamination in the middle looks like a smith that got too fancy stacking and forge welding & didn't want to start over and waste more time on it, rather than a scarf. A scarf near the tang between a less hard & more resilient tang piece, and a hardener blade would not be uncommon or deleterious in a new blade or a repaired blade whose tang had snapped for being too hard. Is that copper or suasa alloy? Looks rather untarnished for copper.
kronckew is offline   Reply With Quote
Old 18th April 2022, 01:54 AM   #4
David R
Member
 
David R's Avatar
 
Join Date: Jan 2011
Posts: 1,079
Default

Quote:
Originally Posted by kronckew View Post
I'd like to see the other side of the blade near the tang/grip. The delamination in the middle looks like a smith that got too fancy stacking and forge welding & didn't want to start over and waste more time on it, rather than a scarf. A scarf near the tang between a less hard & more resilient tang piece, and a hardener blade would not be uncommon or deleterious in a new blade or a repaired blade whose tang had snapped for being too hard. Is that copper or suasa alloy? Looks rather untarnished for copper.
I wondered if it was suasa as well.
David R is offline   Reply With Quote
Old 19th April 2022, 03:31 AM   #5
Battara
EAAF Staff
 
Battara's Avatar
 
Join Date: Dec 2004
Location: Louisville, KY
Posts: 7,226
Default

Only testing will tell for sure.

However, by the hue of the metal, I'm actually leaning toward copper.
Battara is offline   Reply With Quote
Old 19th April 2022, 02:22 PM   #6
CharlesS
Member
 
CharlesS's Avatar
 
Join Date: Dec 2004
Location: Greenville, NC
Posts: 1,857
Default

More pics...definitely polished copper and the scarf weld.
You may have already noticed a considerable number of forging flaws in the pattern weld.
Attached Images
  
CharlesS is offline   Reply With Quote
Old 19th April 2022, 07:22 PM   #7
Ian
Vikingsword Staff
 
Ian's Avatar
 
Join Date: Dec 2004
Location: The Aussie Bush
Posts: 4,203
Default

Charles,

I'm thinking the hilt decoration is a relatively recent redo. The asang asang are not a pair, with the second one looking quite new, and the cord wrap also looks fairly recent to me. The pommel seems older and could be original. The blade itself appears to be 19th C work.
Ian is offline   Reply With Quote
Old 19th April 2022, 11:26 PM   #8
CharlesS
Member
 
CharlesS's Avatar
 
Join Date: Dec 2004
Location: Greenville, NC
Posts: 1,857
Default

Ian, it’s a good point you make. Originally the copper cover was a patinated black. I polished it to get it back to the way it looked originally. It may be a later addition, but the cording is dry rotted and very fragile which lends some credence to its age. I think this is quite an old sword so the fact that it may have seen several grip re-dos would not surprise me at all.
CharlesS is offline   Reply With Quote
Old 30th April 2022, 12:26 AM   #9
Rick
Vikingsword Staff
 
Rick's Avatar
 
Join Date: Nov 2004
Posts: 6,293
Default

Quote:
Originally Posted by CharlesS View Post
You may have already noticed a considerable number of forging flaws in the pattern weld.
The considerable number of flaws makes me wonder if the blade had been broken, and because, for whatever reason, the pattern welded blade was recycled and given a new life.
I also wonder if the pamor patterns have any meaning that could be interpreted as would be found on/in a Jawa keris?

We seem to see more and more Moro swords lately that display manipulated work which, I guess, begs the question about Pamors and whether the Malays/ Moros attributed any powers to them, or whether it was just considered fancy work.
Rick is offline   Reply With Quote
Reply


Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT +1. The time now is 03:09 PM.


Powered by vBulletin® Version 3.8.11
Copyright ©2000 - 2024, vBulletin Solutions Inc.
Posts are regarded as being copyrighted by their authors and the act of posting material is deemed to be a granting of an irrevocable nonexclusive license for display here.