Pusaka · 14th March 2006, 01:04 PM

Thank you Boedhi Adhitya for that information. What is the maximum quantity of meteorite material you could successfully forge a keris with?
I remember being told that meteorite material used to be sold in the market in Solo, Jawa. If so what was that meteorite used for and where did it come from, it is doubtful that it was from the prambanan meteor IMO.

Purwacarita, interesting question. I have often wondered the same. The pamor layers could never be arranged to produce a capacitor effect because a capacitor needs an insulator material between the conductor plates to work. There is no material in the keris blade which would be considered an electrical insulator so producing a capacitor effect using pamor arrangements is not possible.
It is possible that you may get a primitive voltaic pile effect which would produce a miniscule surface current. In that case some pamor types would be better then others at producing it but it would have no practical use.

Thread Tools	Search this Thread
Show Printable Version Email this Page	Search this Thread: Advanced Search
Display Modes
Switch to Linear Mode Switch to Hybrid Mode Threaded Mode

14th March 2006, 01:04 PM	#18
Pusaka Member Join Date: Nov 2005 Posts: 341	Thank you Boedhi Adhitya for that information. What is the maximum quantity of meteorite material you could successfully forge a keris with? I remember being told that meteorite material used to be sold in the market in Solo, Jawa. If so what was that meteorite used for and where did it come from, it is doubtful that it was from the prambanan meteor IMO. Purwacarita, interesting question. I have often wondered the same. The pamor layers could never be arranged to produce a capacitor effect because a capacitor needs an insulator material between the conductor plates to work. There is no material in the keris blade which would be considered an electrical insulator so producing a capacitor effect using pamor arrangements is not possible. It is possible that you may get a primitive voltaic pile effect which would produce a miniscule surface current. In that case some pamor types would be better then others at producing it but it would have no practical use.