Quote:
|
Originally Posted by David
I fear that your restoration approach with this blade may have been far too aggressive...  |
This blade may have been a lost cause before any work was done on it. The only thing that can be done is a chemical cleaning, filing smooth and then finding a way to fill in the pits with metal. I found a shop about five years ago which is willing to try spray welding of on this type of problem. This would be tried in very local areas first. A form of gas welding might work using certain alloys. However it would merely permit re-shaping the blade which would be a reconstruction more than a restoration. It would likely show the alloyed and filed areas as a separate color.
Coin silver has a relatively low melting point. Zinc is even lower. If you are really desperate and have the resources it might be possible to use these metals in sequence. Even an electroplate could be used to fill the final top layer of a filled blade. After finishing the blade would merely look "old and not maintained" instead of like a total disaster. The object is to merely restore the shape and appearance to make a more presentable wall display.
29th January 2012, 05:02 AM
Threaded Mode