I purchased this riveted mail hauberk a while back, the seller claimed it was found in Saudi by an Aramco worker, buried in the sand, while I have no idea if this story is true the hauberk was completely rusted over. I could see none of the usual details which would allow me to identify its origin. I could not see the type of rivets used or if it was completely riveted or if it had alternating rows of solid links. The basic shape did remind me on a very similar hauberk owned by Artzi which he says is Circassian work, the weight was over 20lbs.
I decided to use electricity to remove some of the rust, I was hoping to be able to remove enough to see some details. There are a lot of very detailed descriptions online for this rest removal method, after reading several I got my supplies together, a 5 gallon plastic bucket, 1 computer power supply with two clip ends for positive and negative, a couple of scrap metal pieces for scarificial electrodes, copper wire (steel is recommended), electrolite (Sodium Carbonate) in the form of "washing soda". I put the hauberk in the plastic bucket, and attached the negative wire to it, I then suspended several pieces of scrap metal around the inside of the bucket making sure that they did not touch the hauberk these were attached to the positive wire, I added water to the top with 1 table spoon of electrolite for each gallon. I plugged in the power supply (outdoors) and tiny bubbles started to appear, a sign that everything was connected correctly. It did not take long for a very thick surface of corrosion to appear on the top of the water which I poured off occasionally, after around 24 hrs I removed the hauberk and washed it off, I used a blower to get as much of the water off as I could before it started to rust again, which I was told would happen quite quickly, I then coated the entire surface with "Break Free" spray. The results were quite dramatic, I could now see that this was a very well made hauberk with alternating rows of solid links and what appears to be wedge riveted links, the links are very uniform in size and shape and quite well made. Normally wedge rivets would indicate European origin but there are some examples of Circassian mail with wedge riveting including a few examples in the Mets collection. European mail would not use alternating rows of solid links after around the late 14th to early 15th century but Indo-Persian mail commonly used solid links but with round rivets not wedge rivets. Circassians were known to make mail for the Ottomans but more research will be needed. I will have to do another round of rust removal, I will probably use the same method. |
![]() |
![]() |
![]() |
#2 |
Member
Join Date: Jul 2010
Location: St. Louis, MO area.
Posts: 1,623
|
![]()
Hi Estcrh.
WOW!! What a difference !!! Great job. That process really does work. Yes, another application would be worth a try. Would be interesting to see if a second application takes any more off. Another method I found very effective for removing loose, red rust is glass bead blasting (not sand blasting). You can set the air gun to very slow speed and remove as little or as much as you want. And it does so without removing the original patina. However, in the case of this Hauberk, with the small links close together, I would think that your electrolysis method would be easier and more effective. And it appears so. Again, great job. It still amazes me how long the Caucasions/Circasions continued to use mail armour. At least according to photographic evidence, all the up to the 1870/80's. Again, a really nice addition to your collection. Rick. |
![]() |
![]() |
![]() |
#3 | |
Member
Join Date: Jun 2012
Location: USA
Posts: 1,497
|
![]() Quote:
I wasnt sure how far the rust went, luckly there is still a lot of metal left, I will post some additional pictures whenever I get around to treating it again. This method can be used on weapons as well, I have seen some really incredible results on dug up iron objects that were heavily corroded, also on old tools and auto parts. |
|
![]() |
![]() |
![]() |
#4 |
Member
Join Date: Jan 2016
Location: Chino, CA.
Posts: 217
|
![]()
Isn't Indo-Persain maille usually bar-link?
|
![]() |
![]() |
![]() |
#5 | ||
Member
Join Date: Jun 2012
Location: USA
Posts: 1,497
|
![]() Quote:
Below are some images of theta links from an Indian example and a report from the Royal Armouries. Notice the extreme small size of the individual links, making it next to impossible for even an arrow head to pass through. Quote:
Last edited by estcrh; 18th June 2016 at 05:11 AM. |
||
![]() |
![]() |
![]() |
#6 |
EAAF Staff
Join Date: Dec 2004
Location: Louisville, KY
Posts: 7,186
|
![]()
W
![]() That's crazy! |
![]() |
![]() |
![]() |
|
|