Thanks for that research Geoff, much appreciated, it reveals a lot to me .
...... so metallurgical technospeak aside.. that tells me that the core of this weapon was quite pure low carb iron and that the PW contrast was due to phosphourous containing iron welded (piled) with a purer iron without any phosphorous inclusions in it.
so far so good... I wonder what would happen if you bent said blade over your knee ? So much pure iron in it would surely dictate a set (ie remained bent) blade after say 5 inches out of true over the 30 inches of the blades length ??. Being hammered so thin at the tip for a good cut would mean a susceptability to incur this type of deformation in use. Easiest way to stop this is to make a thicker non flexable blade ?? any comments ?
|