Bill · 15th March 2005, 06:02 PM

Dr. Ann as well as anyone else that will comment. What can todays research tell us about these swords. My interest is really about the "Moro" kris. There seems to have been receint research into "luwa" iron, mostly from the folks from Australian National University. What info can we find from examples without any providence. Can you comment on what can be found from iron. This has been discussed in the past, it would seem age is not obtainable, only whether something is consistant for that period. Rust seems to be testable but in your opinion, how well, & how much is needed. I have a few very old "Moro" kris & wonder what is possible to find out about them. How much of something needs to be "sacrificed"? With the dress of these swords is wood, ratten, buffalo horn, deer antler, & in one case I have a sheath wrapped in leaves, but one may assume the dress may not indicate the age of the metal but does add to the picture. I have a 16" "Moro" kris that the guard has already been broken, the hilt has been broken, the tang repaired & even the old injuries have a deep patina that suggests conciderable age. The sword would be expendable if valid info could be found. What can be found to determine age, & what & how much would be lost in order to do so (like a small part of the tang or chip from the inside of a hilt? Is it possible to do ascertain pieces made without European iron? Thank You.

Andrew · 15th March 2005, 07:28 PM

An excellent question, Bill, and one I'm eager for an answer to, as well.

Conogre · 16th March 2005, 08:53 AM

I have to admit to being slightly puzzzled by what you mean by "testable".
If you're referring to carbon 14 tests and such, tests of this nature usually aren't indicated except in pieces of great antiquity, with swords in the 100,200 and 300 years being unsuitable altogether by being simply too new.
With wood, for example, what you will get is the age of the wood itself, not when a hilt was made.
Mike

Ann Feuerbach · 16th March 2005, 06:23 PM

Hi Bill,
Excuse me if this answer is a bit muddled, I have a horrible cold and a fuzzy head

In the future we may be able to carbon date iron, I know Oxford has been working on this with varing amounts of success. Ideally a small uncorroded sample can tell us information such as if there is slag inclusions. The type of slag could in some circumstances suggest a relative date. Elemental analysis can also sometimes suggest whether or not it is new or old iron. We can also tell about the iron/carbon content and heat treatments. Testing rust will only tell you it is iron. Due to segretation and leaching in and out of elements during corrosion, as far as I know you can not get any useful information out of rust. I would be very scptical about any one who says they can learn alot from corrosion. I have found relic structures in corrosion products. It is hard to say what can be learnt about it without seeing it. If you want, send it to me and I can take a look at it and suggest possible aspects for research.
Ann

Bill · 16th March 2005, 08:08 PM

Thank You, Dr. Ann

B.I · 16th March 2005, 10:50 PM

ann,
i recall a conversation with david edge a few years back (quite a few) when he said the same thing. from scant memory, isnt the new/old iron down to a specific date, where iron technology changed. or, is this refering to european iron or steel which is more davids speciality. i remember him saying the date, but only remember it being around the end of the 19thC. if this branches past european, then surely this is useful information to some, whose sphere centres around the 19th/20thC

Ann Feuerbach · 16th March 2005, 11:09 PM

Bloomery iron and bloomery slag is different than blast furnace iron and blast furnace slag, and both differ from modern more refined steels, in elemental compostion and often in structure/phases. It is not always easy to tell them apart through microstructure or elemental compostion, but people have studied the differences with some success. I did a bit of a review in my PhD on that if you or anyone wants more details. For dates, particularly more modern ones, I'd have to look it up.
Ann

Marc · 17th March 2005, 12:05 AM

I think Mr. Edge could have been referring to the Bessemer Process that about the 1870's started to flood the market with cheap and almost slag-free steel. The presence or absence of slag would then be a first indicator about the authenticity of a particular object. Not definitive, but at least significative enough. Specially taken in the right context: this kind of steel was, for example, frequently used to make parts for armour in order to "complete" it, at the end of the 19th - beginning of 20th. Not necessarily with an evil intent, but after so much time it's sometimes hard to tell apart what's new-ish and what's not, so this kind of examination can help. Again, not definitive, but it's, let's say, "another tool in the box".

Ann Feuerbach · 17th March 2005, 02:39 PM

Yes, I agree.

RSWORD · 17th March 2005, 05:25 PM

Quote:

Originally Posted by Ann Feuerbach

Hi Bill,
Excuse me if this answer is a bit muddled, I have a horrible cold and a fuzzy head

In the future we may be able to carbon date iron, I know Oxford has been working on this with varing amounts of success. Ideally a small uncorroded sample can tell us information such as if there is slag inclusions. The type of slag could in some circumstances suggest a relative date. Elemental analysis can also sometimes suggest whether or not it is new or old iron. We can also tell about the iron/carbon content and heat treatments. Testing rust will only tell you it is iron. Due to segretation and leaching in and out of elements during corrosion, as far as I know you can not get any useful information out of rust. I would be very scptical about any one who says they can learn alot from corrosion. I have found relic structures in corrosion products. It is hard to say what can be learnt about it without seeing it. If you want, send it to me and I can take a look at it and suggest possible aspects for research.
Ann

In regards to using corrosion to date a blade, it might be worth mentioning, that it is the accepted method of dating Japanese blades through the examination of the corrosion on the tang. I think a lot of study as been put into this over the years and one can start seeing trends in the depth of corrosion, color of corrosion, etc. and match this to dated tangs to get an "eye" for dating an unsigned blade. Barring new technology that can somehow date the metal of the blade, studying a blades tang seems to be an accepted method of dating. Thoughts?

Jens Nordlunde · 17th March 2005, 06:27 PM

RSword,
I don’t quite agree with you, although I don’t know much about it, what if the blade had been keep clean and oiled, but the sword itself had been kept in a rather damp place, then the tang would have more corrosion than another sword, also oiled and cleaned, but having been kept in a dry place. Don’t you think?

Jens

Andrew · 17th March 2005, 06:43 PM

I think both Rick and Jens raise interesting and valid points. My suspicion is that tang condition is but one of several elements used to date a Japanese sword. In other words, tang condition, by itself is useful data. Just not definitive.

Comments from Rich on this would be helpful.

Ann Feuerbach · 17th March 2005, 06:44 PM

Perhaps under certain circumstances it may be possible to suggest a date by corrosion, but having spent alot of time with corrosion (during my conservation degree). It would not rely on it. It is so easy to corode something. That said, you can look at the type and depth of corrosion which may suggest if it is genuine or fake, things like intergranular corrosion and what form the iron oxide is in, and if there is any relic stuctures in corrosion products, these factors I believe usually occur during slow corrosion. I have some iron that has been in my garage for only a few years (old file I did not want my mom to toss out, but even in the garage after a short time, they have totally lost their shape. They are even too far gone for me to even attempt to conserve.

Yannis · 17th March 2005, 06:45 PM

Quote:

Originally Posted by Jens Nordlunde

...the sword itself had been kept in a rather damp place...

Jens, in Japanese swords circles this is a blasphemy

Jens Nordlunde · 17th March 2005, 07:28 PM

Yannis, I am sure it is, but some people live near the sea, and som inland - that should give a difference, if maybe only a small one - but over the years?

Jens

Bill · 17th March 2005, 07:41 PM

My original question was in referance to: http://www.tms.org/pubs/journals/JOM...Cook-0305.html , but seems to be less than perfect. I've also read there is some debate to when the "luwa" (Sulawesi) smelting started. Is thermoluminescence viable for these studies or is it just to expensive for Universities for results that still would be questioned.

wolviex · 17th March 2005, 09:09 PM

Quote:

Originally Posted by Bill

What can be found to determine age, & what & how much would be lost in order to do so (like a small part of the tang or chip from the inside of a hilt? Is it possible to do ascertain pieces made without European iron? Thank You.

Let me join to this interesting discussion for a while. According to the quote above I'll tell you a story from a Polish museum. It was probably in the 50's (I know it from the tales also, too young to remember

), when some metallurgist came to the museum and offered to examin excavated 11th century sword. Director, a very known Polish weapon scholar in those days, wasn't convinced about safety and legitimacy of such experience. But this metallurgist attained his goal promising to learn everything about this sword, mativated such examine as very important for Polish science, metallurgy etc. Then, with the director's permission in one hand and file in another, he just cut off 4 cm of the tang

After few weeks he send to the musuem a piece of paper with few notes of chemistry symbols with percents - something what should every classical scholar (this director was one of them) bring to heart attack. Nothing more. No age, no nothing - just inexplicable percents. To be honest I don't know what happened to this piece of paper with such important science results - I can imagine that director tread it into the ground

. Now this sword, with ugly cut tang, is visible on our arms and armour exhibition - for someones as a specific warning

Nowadays, as far as I know, there are non-invasive methods.

About the rust - I heard from reliable sources about fakers which are meaking very beautiful, old, deep corrosion

- so be careful

Best regards

Jens Nordlunde · 17th March 2005, 09:28 PM

Long time ago I heard that cowdung should be very good when aging blades/tangs.

Jens

Bill · 17th March 2005, 09:44 PM

Well my thoughts were that when an old hilt is removed there is usually conciderable rust that is going to be removed any way, nice if it could have purpose.

Andrew · 17th March 2005, 10:46 PM

Quote:

Originally Posted by Jens Nordlunde

Long time ago I heard that cowdung should be very good when aging blades/tangs.

Jens

How ironic.

Federico · 18th March 2005, 08:29 AM

Quote:

Originally Posted by wolviex

Let me join to this interesting discussion for a while. According to the quote above I'll tell you a story from a Polish museum. It was probably in the 50's (I know it from the tales also, too young to remember

), when some metallurgist came to the museum and offered to examin excavated 11th century sword. Director, a very known Polish weapon scholar in those days, wasn't convinced about safety and legitimacy of such experience. But this metallurgist attained his goal promising to learn everything about this sword, mativated such examine as very important for Polish science, metallurgy etc. Then, with the director's permission in one hand and file in another, he just cut off 4 cm of the tang

After few weeks he send to the musuem a piece of paper with few notes of chemistry symbols with percents - something what should every classical scholar (this director was one of them) bring to heart attack. Nothing more. No age, no nothing - just inexplicable percents. To be honest I don't know what happened to this piece of paper with such important science results - I can imagine that director tread it into the ground

. Now this sword, with ugly cut tang, is visible on our arms and armour exhibition - for someones as a specific warning

Nowadays, as far as I know, there are non-invasive methods.

About the rust - I heard from reliable sources about fakers which are meaking very beautiful, old, deep corrosion

- so be careful

Best regards

I got to admit, this story made me teary eyed.

Rich · 18th March 2005, 11:37 AM

"In regards to using corrosion to date a blade, it might be worth mentioning,
that it is the accepted method of dating Japanese blades through the
examination of the corrosion on the tang. I think a lot of study as been put
into this over the years and one can start seeing trends in the depth of
corrosion, color of corrosion, etc. and match this to dated tangs to get an
"eye" for dating an unsigned blade. Barring new technology that can
somehow date the metal of the blade, studying a blades tang seems to be an
accepted method of dating. Thoughts?"

----------

The type of rust, extent of rust and color of rust is
used as an aid in dating Japanese swords. However, everyone
realizes that it can be "faked". In Nihonto circles it is
bad to ever clean the tang of a sword since it is used
in dating. The basic guidelines (just that - guidelines)
are in order of recent to oldest: red rust, brown rust,
rough black rust, smooth black rust. Again though I must
mention, as has been said, it is just one aspect of dating
the sword and is not considered absolute by any means.
Other things considered are shape, prominence of hada (grain
in the folding process), style of hamon (temperline), among
others. None of these are absolute and any or all can be
replicated by modern smiths. That why we have shinsa
(judging) by a group of Japanese experts and even then
errors are sometimes made.

Interesting thread. I wish there was a simple, fool proof
method of dating blades of any culture. It would sure
simplify things. How about all the "bronze age" fakes on
the market?

Rich S
------------------------------------------------------------
Richard Stein, PhD alchemyst@yahoo.com

The Japanese Sword Index
http://www.geocities.com/alchemyst/nihonto.htm
------------------------------------------------------------

Ann Feuerbach · 18th March 2005, 03:01 PM

Thanks Bill for the link to that article...it is great and a lot to take in. I think for the time being, stylistic studies, along with technological studies, will be the only way for us to date iron for a while. The radiocarbon does show promise. What I feel is needed is more research/database on styles etc... Then it would be easier to compare authenitic objects with questionable ones.

15th March 2005, 06:02 PM	#1
Bill Member Join Date: Feb 2005 Location: Chicago area Posts: 327	Dr. Ann, Dr. Ann Dr. Ann as well as anyone else that will comment. What can todays research tell us about these swords. My interest is really about the "Moro" kris. There seems to have been receint research into "luwa" iron, mostly from the folks from Australian National University. What info can we find from examples without any providence. Can you comment on what can be found from iron. This has been discussed in the past, it would seem age is not obtainable, only whether something is consistant for that period. Rust seems to be testable but in your opinion, how well, & how much is needed. I have a few very old "Moro" kris & wonder what is possible to find out about them. How much of something needs to be "sacrificed"? With the dress of these swords is wood, ratten, buffalo horn, deer antler, & in one case I have a sheath wrapped in leaves, but one may assume the dress may not indicate the age of the metal but does add to the picture. I have a 16" "Moro" kris that the guard has already been broken, the hilt has been broken, the tang repaired & even the old injuries have a deep patina that suggests conciderable age. The sword would be expendable if valid info could be found. What can be found to determine age, & what & how much would be lost in order to do so (like a small part of the tang or chip from the inside of a hilt? Is it possible to do ascertain pieces made without European iron? Thank You.

Thread Tools	Search this Thread
Show Printable Version Email this Page	Search this Thread: Advanced Search
Display Modes
Linear Mode Switch to Hybrid Mode Switch to Threaded Mode

15th March 2005, 07:28 PM	#2
Andrew Member Join Date: Nov 2004 Location: USA Posts: 1,725	An excellent question, Bill, and one I'm eager for an answer to, as well.

16th March 2005, 08:53 AM	#3
Conogre Member Join Date: Feb 2005 Location: Clearwater, Florida Posts: 371	I have to admit to being slightly puzzzled by what you mean by "testable". If you're referring to carbon 14 tests and such, tests of this nature usually aren't indicated except in pieces of great antiquity, with swords in the 100,200 and 300 years being unsuitable altogether by being simply too new. With wood, for example, what you will get is the age of the wood itself, not when a hilt was made. Mike

16th March 2005, 06:23 PM	#4
Ann Feuerbach Member Join Date: Feb 2005 Posts: 133	Hi Bill, Excuse me if this answer is a bit muddled, I have a horrible cold and a fuzzy head In the future we may be able to carbon date iron, I know Oxford has been working on this with varing amounts of success. Ideally a small uncorroded sample can tell us information such as if there is slag inclusions. The type of slag could in some circumstances suggest a relative date. Elemental analysis can also sometimes suggest whether or not it is new or old iron. We can also tell about the iron/carbon content and heat treatments. Testing rust will only tell you it is iron. Due to segretation and leaching in and out of elements during corrosion, as far as I know you can not get any useful information out of rust. I would be very scptical about any one who says they can learn alot from corrosion. I have found relic structures in corrosion products. It is hard to say what can be learnt about it without seeing it. If you want, send it to me and I can take a look at it and suggest possible aspects for research. Ann

16th March 2005, 08:08 PM	#5
Bill Member Join Date: Feb 2005 Location: Chicago area Posts: 327	Thank You, Dr. Ann

16th March 2005, 10:50 PM	#6
B.I Member Join Date: Jan 2005 Posts: 485	ann, i recall a conversation with david edge a few years back (quite a few) when he said the same thing. from scant memory, isnt the new/old iron down to a specific date, where iron technology changed. or, is this refering to european iron or steel which is more davids speciality. i remember him saying the date, but only remember it being around the end of the 19thC. if this branches past european, then surely this is useful information to some, whose sphere centres around the 19th/20thC

16th March 2005, 11:09 PM	#7
Ann Feuerbach Member Join Date: Feb 2005 Posts: 133	Bloomery iron and bloomery slag is different than blast furnace iron and blast furnace slag, and both differ from modern more refined steels, in elemental compostion and often in structure/phases. It is not always easy to tell them apart through microstructure or elemental compostion, but people have studied the differences with some success. I did a bit of a review in my PhD on that if you or anyone wants more details. For dates, particularly more modern ones, I'd have to look it up. Ann

17th March 2005, 12:05 AM	#8
Marc Member Join Date: Dec 2004 Location: Madrid / Barcelona Posts: 256	I think Mr. Edge could have been referring to the Bessemer Process that about the 1870's started to flood the market with cheap and almost slag-free steel. The presence or absence of slag would then be a first indicator about the authenticity of a particular object. Not definitive, but at least significative enough. Specially taken in the right context: this kind of steel was, for example, frequently used to make parts for armour in order to "complete" it, at the end of the 19th - beginning of 20th. Not necessarily with an evil intent, but after so much time it's sometimes hard to tell apart what's new-ish and what's not, so this kind of examination can help. Again, not definitive, but it's, let's say, "another tool in the box".

17th March 2005, 02:39 PM	#9
Ann Feuerbach Member Join Date: Feb 2005 Posts: 133	Yes, I agree.

17th March 2005, 06:27 PM	#11
Jens Nordlunde Member Join Date: Dec 2004 Location: Europe Posts: 2,718	RSword, I don’t quite agree with you, although I don’t know much about it, what if the blade had been keep clean and oiled, but the sword itself had been kept in a rather damp place, then the tang would have more corrosion than another sword, also oiled and cleaned, but having been kept in a dry place. Don’t you think? Jens

17th March 2005, 06:43 PM	#12
Andrew Member Join Date: Nov 2004 Location: USA Posts: 1,725	I think both Rick and Jens raise interesting and valid points. My suspicion is that tang condition is but one of several elements used to date a Japanese sword. In other words, tang condition, by itself is useful data. Just not definitive. Comments from Rich on this would be helpful.

17th March 2005, 06:44 PM	#13
Ann Feuerbach Member Join Date: Feb 2005 Posts: 133	Perhaps under certain circumstances it may be possible to suggest a date by corrosion, but having spent alot of time with corrosion (during my conservation degree). It would not rely on it. It is so easy to corode something. That said, you can look at the type and depth of corrosion which may suggest if it is genuine or fake, things like intergranular corrosion and what form the iron oxide is in, and if there is any relic stuctures in corrosion products, these factors I believe usually occur during slow corrosion. I have some iron that has been in my garage for only a few years (old file I did not want my mom to toss out, but even in the garage after a short time, they have totally lost their shape. They are even too far gone for me to even attempt to conserve.

17th March 2005, 07:28 PM	#15
Jens Nordlunde Member Join Date: Dec 2004 Location: Europe Posts: 2,718	Yannis, I am sure it is, but some people live near the sea, and som inland - that should give a difference, if maybe only a small one - but over the years? Jens

17th March 2005, 07:41 PM	#16
Bill Member Join Date: Feb 2005 Location: Chicago area Posts: 327	My original question was in referance to: http://www.tms.org/pubs/journals/JOM...Cook-0305.html , but seems to be less than perfect. I've also read there is some debate to when the "luwa" (Sulawesi) smelting started. Is thermoluminescence viable for these studies or is it just to expensive for Universities for results that still would be questioned.

17th March 2005, 09:28 PM	#18
Jens Nordlunde Member Join Date: Dec 2004 Location: Europe Posts: 2,718	Long time ago I heard that cowdung should be very good when aging blades/tangs. Jens

17th March 2005, 09:44 PM	#19
Bill Member Join Date: Feb 2005 Location: Chicago area Posts: 327	Well my thoughts were that when an old hilt is removed there is usually conciderable rust that is going to be removed any way, nice if it could have purpose.

18th March 2005, 11:37 AM	#22
Rich Member Join Date: Dec 2004 Location: comfortably at home, USA Posts: 432	"In regards to using corrosion to date a blade, it might be worth mentioning, that it is the accepted method of dating Japanese blades through the examination of the corrosion on the tang. I think a lot of study as been put into this over the years and one can start seeing trends in the depth of corrosion, color of corrosion, etc. and match this to dated tangs to get an "eye" for dating an unsigned blade. Barring new technology that can somehow date the metal of the blade, studying a blades tang seems to be an accepted method of dating. Thoughts?" ---------- The type of rust, extent of rust and color of rust is used as an aid in dating Japanese swords. However, everyone realizes that it can be "faked". In Nihonto circles it is bad to ever clean the tang of a sword since it is used in dating. The basic guidelines (just that - guidelines) are in order of recent to oldest: red rust, brown rust, rough black rust, smooth black rust. Again though I must mention, as has been said, it is just one aspect of dating the sword and is not considered absolute by any means. Other things considered are shape, prominence of hada (grain in the folding process), style of hamon (temperline), among others. None of these are absolute and any or all can be replicated by modern smiths. That why we have shinsa (judging) by a group of Japanese experts and even then errors are sometimes made. Interesting thread. I wish there was a simple, fool proof method of dating blades of any culture. It would sure simplify things. How about all the "bronze age" fakes on the market? Rich S ------------------------------------------------------------ Richard Stein, PhD alchemyst@yahoo.com The Japanese Sword Index http://www.geocities.com/alchemyst/nihonto.htm ------------------------------------------------------------

18th March 2005, 03:01 PM	#23
Ann Feuerbach Member Join Date: Feb 2005 Posts: 133	Thanks Bill for the link to that article...it is great and a lot to take in. I think for the time being, stylistic studies, along with technological studies, will be the only way for us to date iron for a while. The radiocarbon does show promise. What I feel is needed is more research/database on styles etc... Then it would be easier to compare authenitic objects with questionable ones.