#1 |
Member
Join Date: Mar 2017
Posts: 444
|
![]()
I am very wary of purchasing kukri from online auctions because I find it hard to determine the older ones from more modern versions (or outright fakes). However, I took a chance on this one because it seemed to have genuine age.
What do you all think? Someone polished all the patina (if there was any) off of the blade. I appreciate that they didn't polish it down smooth, as it has a texture I quite like. The grip is of some kind of horn/antler. Can someone help identify? That too seems to have some legitimate age. Here are some specs: Overall length - approx 18" Blade length - approx. 13" Blade thickness - 6mm across the spine at the hilt Weight - 1lb 2.375oz. As always, apologies for the quality of the photos. Thanks for sharing your thoughts and impressions. |
![]() |
![]() |
![]() |
#2 |
Vikingsword Staff
Join Date: Nov 2004
Posts: 6,284
|
![]()
How old do you think it is?
It's very hard to guess due to the condition issues, but I'd guess very early 20th century. |
![]() |
![]() |
![]() |
#3 | |
Member
Join Date: Mar 2017
Posts: 444
|
![]() Quote:
|
|
![]() |
![]() |
![]() |
#4 |
Vikingsword Staff
Join Date: Nov 2004
Posts: 6,284
|
![]()
Here is a kukri that is probably first quarter of the 20thC; it was bought at a barn sale in New England some years ago.
I believe your kukri has been badly neglected I'm sorry to say, and that doesn't help things as far as judging age goes. ![]() |
![]() |
![]() |
![]() |
#5 |
Member
Join Date: Jan 2011
Posts: 1,065
|
![]()
Acid dipped.
|
![]() |
![]() |
![]() |
#6 | |
Member
Join Date: Apr 2005
Posts: 3,249
|
![]() Quote:
As Rick, I'd also guess this piece got badly neglected. Considering that the damage to the horn is pretty much unilateral, I wonder if this kukhri got exposed to exessive heat from fire/etc. and then left in some basement rotting away... Regards, Kai |
|
![]() |
![]() |
![]() |
#7 |
Member
Join Date: Apr 2019
Posts: 98
|
![]()
Earliest would be ww2 period and likely something that came out of an Indian bazaar (market) originally. Brass bolster, poor fuller work and horn hilt etc. In relic condition because it has been neglected badly and I hope you did not pay much for it.
|
![]() |
![]() |
![]() |
#8 | |
Member
Join Date: Jun 2013
Posts: 2,145
|
![]() Quote:
As Jim mentionned many times, the problem with ethno weapons is: it's not because they look old that they are old... African and Arab weapons look old because they were worn with a poor maintenance. For your Indian kukri it's just a problem of conservation. |
|
![]() |
![]() |
![]() |
#9 | |
Member
Join Date: Jan 2011
Posts: 1,065
|
![]() Quote:
|
|
![]() |
![]() |
![]() |
#10 |
Member
Join Date: Apr 2005
Posts: 3,249
|
![]()
Then I'd expect more surface corrosion at the brass bolster, David.
Humidty and neglect can be hard enough on carbon steel. Regards, Kai |
![]() |
![]() |
![]() |
#11 |
Member
Join Date: Jan 2007
Posts: 803
|
![]()
The kukri has a nice overall shape.
Gents, Do you think there is any chance it was in a fire? The hilt looks rather charred to me...... |
![]() |
![]() |
![]() |