I appreciate the comments. I thought there was something terribly wrong when I saw the streaks running counter to the grain of the steel, but wasn't sure if this was a bad attempt at faking the layers or was some common decorative treatment that I had never heard of.
In any case, Under magnification, I can see that the bright lines stand slightly proud of the background (maybe .001" or thereabouts). I suppose if the wax resist was used, it protected the steel from being etched where the lines occur. I don't know if cleaning the blade at this point would make the lines disappear or not. I don't like the idea of using abrasives to remove them, so I may just stain them as best I can to make it less obtrusive. Any suggestions are welcome.
Thanks for your help,
DD
|