Quote:
Originally Posted by Marc M.
Sorry for my late response, in my opinion it is indeed not damascus but as you said it looks like the structure of hot steel cooled in water or oil. Try if you can bend the blade a little, does it come back straight, steel, does it stand crooked, iron.
|
Thank you Marc!
My intention is not to make Rob's koummya bad, but to make it clear that what we see here is in no way a lamination in any way.
Regards,
Detlef