Hi Jeff, Greg and Ann,
No you, Greg and Ann are not the only ones interested in this subject – I am too. Only my knowledge about the subject is far too little to join the discussion, other than ask the stupid questions – so that is what I will do.
How about one of you writing a ‘Wootz for Dummies’, that might help many of us.
Is it so, that in theory sham has less carbon than 0.8, and wootz has more than 0.8?
When I write ‘in theory’ it is be course of what Greg wrote. I have understood that the smith, if the difference of carbon is not too big, can make a blade after his own wishes, is that correct? Earlier this was of course impossible, as they could not measure the carbon.
When the crucibles were made ready for melting, this of course would mean that none of them would be exactly the same, as the amount of organic stuff you put into each could/would differ from crucible to crucible, also meaning that the man maintaining the work had to be very accurate. Some were, others were not. This could explain what I have read about the Arabian merchants having people living in India to check the crucibles before they were exported – as some were of a lesser quality.
|